• Deposits extremely hard weld metal with a martensitic structure.
  • The weld metal contains dispersed carbides and borides.
  • It’s used for abrasion resistance beyond what regular martensitic weld metal can handle.
  • Multiple layers can’t be applied due to decreased crack resistance.
  • Machining the weld metal immediately after welding is not possible.